| Customization: | Available |
|---|---|
| Color: | Green |
| Appearance: | Solvent |
|
Still deciding? Get samples of US$ 100/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
SPR is a R&D and manufacturing enterprise of industrial building materials with rich experience. The company integrates product research and development, production, sales, technical services, design and construction. From the perspective of the market and the actual needs of customers, it conducts special investigation, integration, and implementation of integrated process operations. Every step strives to improve, and strives to provide customers with innovative system solutions and high-quality products. SPR Fine Chemicals (Guangdong) Co., Ltd. is located in Nanxiong High-tech Zone, Guangdong Province, covering an area of more than 20000 square meters, with an annual output of 16000 tons. In 2022, SPR and Guangdong Kin Long Hardware Products Co., Ltd. reached strategic cooperation in the form of equity participation, and jointly established Guangdong Kin Long SPR Construction Engineering Co., Ltd to create a one-stop service model for the industry chain of the floor industry.
Polyurethane universal self-leveling mortar is a four component color water-based self-leveling mortar floor coating made with high-performance polyurethane resin as the base material, and special cement, graded silica sand, and active pigments as the aggregates; Excellent impact resistance, damage resistance, chemical resistance, and scrub resistance
Base Surface Treatment
The treatment of base concrete is the key to making a good polyurethane concrete floor. The quality of ground treatment directly affects the service life of the floor. In order to enhance the adhesion between the base and the floor, mechanical treatment is required to expose concrete aggregates (such as shot blasting). The floor surface must be grooved, with the depth and width of the groove being 2-3 times the thickness of the polyurethane mortar floor; In particular, all edges (such as trenches, etc.) should be grooved at a distance of 20mm;
Primer Application
After the base surface is cleaned, mix the SPR-23101P polyurethane universal self-leveling mortar material evenly according to the design ratio, pour another bucket for mixing again, and then use the scraping and coating method for batch scraping construction. Strictly control the filling of each groove and gap. After mixing the material, use a trowel to continuously pave it. This step cannot be interrupted, and needs to be completed as soon as possible to ensure better adhesion of the material. To ensure that the base layer is completely sealed, a primer of polyurethane on a thickness of 1mm is suitable;
Grinding After Solidification Of The Primer
After solidification of the polyurethane mortar primer, it is necessary to grind the rough primer with a grinder to increase the adhesion between subsequent coatings;
Construction Of Polyurethane Mortar Surface Coating
evenly mix SPR-23101P polyurethane universal self-leveling mortar according to the proportion (using a low-speed double-head or spiral blade mixer), pour another bucket for mixing again, use a nail rake to evenly spread the material according to a certain thickness, use a spatula to pave, and use a defoaming roller to roll back and forth. After mixing the material, continue to apply it. This step cannot be interrupted, and needs to be completed as soon as possible, To ensure better surface effect and adhesion.
| No. | Test Item | Testing Reference | Judgment Criteria | Unit | Test Result | Judgment |
|---|---|---|---|---|---|---|
| 1 | Container Condition | GB/T22374-2018 | Component A: Uniform state after stirring, no hard lumps | Conforms | Qualified | |
| Component B: Uniform state after stirring, no hard lumps | Conforms | Qualified | ||||
| Component C: Uniform state after stirring, no hard lumps | Conforms | Qualified | ||||
| Component D: Uniform state after stirring, no hard lumps | Conforms | Qualified | ||||
| 2 | Coating Appearance | GB/T22374-2018 | Surface smooth and uniform, no visible shrinkage, floating color, wrinkles, pinholes, cracks, etc. | Conforms | Qualified | |
| 3 | Drying Time | GB/T1728-1979 | Surface Dry: ≤8h (8ºC) | h | Conforms | Qualified |
| Hard Dry: ≤48h (48°C) | h | Conforms | Qualified | |||
| 4 | Abrasion Resistance | GB/T1768-2006 | ≤0.050g | g | 0.042 | Qualified |
| 5 | Tensile Adhesion Strength | GB/T22374-2018 | ≥2.0MPa | MPa | 2.0 | Qualified |
| 6 | Impact Resistance | GB/T22374-2018 | No cracks, no peeling | Conforms | Qualified | |
| 7 | Water Resistance (168h) | GB/T9274-1988 | No blistering, no peeling, slight discoloration allowed, recovers after 2h | Conforms | Qualified |